透明运动鞋底 滑雪膜应用 高粘度 热和光稳定 PA12 赢创德固赛 LX9012

Physical Properties	Metric	English	Comments
Density 	1.01 g/cc	0.0365 lb/in3	ISO 1183
Moisture Absorption at Equilibrium 	0.80 %	0.80 %	50% RH; ISO 62
Water Absorption at Saturation 	1.5 %	1.5 %	ISO 62
Linear Mold Shrinkage, Flow 	0.010 cm/cm	0.010 in/in	ISO 294-4
Linear Mold Shrinkage, Transverse 	0.014 cm/cm	0.014 in/in	ISO 294-4
 
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break 	46.0 MPa	6670 psi	ISO 527-1/-2
Tensile Strength, Yield 	37.0 MPa	5370 psi	ISO 527-1/-2
Elongation at Break 	>= 50 %	>= 50 %	ISO 527-1/-2
Elongation at Yield 	5.0 %	5.0 %	ISO 527-1/-2
Tensile Modulus 	1.10 GPa	160 ksi	ISO 527
Charpy Impact Unnotched  	NB
@Temperature 23.0 °C	NB
@Temperature 73.4 °F	ISO 179/1eU
 	NB
@Temperature -30.0 °C	NB
@Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched  	1.30 J/cm2
@Temperature 23.0 °C	6.19 ft-lb/in2
@Temperature 73.4 °F	ISO 179/1eA
 	1.30 J/cm2
@Temperature -30.0 °C	6.19 ft-lb/in2
@Temperature -22.0 °F	ISO 179/1eA
 
Electrical Properties	Metric	English	Comments
Volume Resistivity 	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Dielectric Constant  	3.0
@Frequency 1.00e+6 Hz	3.0
@Frequency 1.00e+6 Hz	ISO 60250
 	3.8
@Frequency 100 Hz	3.8
@Frequency 100 Hz	ISO 60250
Dielectric Strength 	24.0 kV/mm	610 kV/in	K20/P50; IEC 60423-1
Dissipation Factor  	0.028
@Frequency 1.00e+6 Hz	0.028
@Frequency 1.00e+6 Hz	IEC 60250
 	0.053
@Frequency 100 Hz	0.053
@Frequency 100 Hz	IEC 60250
 
Thermal Properties	Metric	English	Comments
CTE, linear 	234 μm/m-°C
@Temperature 23.0 - 55.0 °C	130 μin/in-°F
@Temperature 73.4 - 131 °F	ISO 11359
Melting Point 	176 °C	349 °F	ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 	120 °C	248 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 	45.0 °C	113 °F	ISO 75
Vicat Softening Point  	130 °C
@Load 5.10 kg	266 °F
@Load 11.2 lb	Method B; ISO 306
 	170 °C
@Load 1.02 kg	338 °F
@Load 2.25 lb	Method A; ISO 306
Flammability, UL94  	HB
@Thickness 1.60 mm	HB
@Thickness 0.0630 in	IEC 60695
 	HB
@Thickness 3.20 mm	HB
@Thickness 0.126 in	IEC 60695