液压离合器管路等承受较高温度的管路系统应用 耐冲击 热和光稳定 PA612 赢创德固赛 DX9304

 
Physical Properties	Metric	English	Comments
Density 	1.04 g/cc	0.0376 lb/in3	ISO 1183
Moisture Absorption at Equilibrium 	1.0 %	1.0 %	50% RH; ISO 62
Water Absorption at Saturation 	2.7 %	2.7 %	ISO 62
 
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield 	50.0 MPa	7250 psi	ISO 527-2/1A
Elongation at Break 	>= 50 %	>= 50 %	ISO 527-2/1A
Elongation at Yield 	5.0 %	5.0 %	ISO 527-2/1A
Tensile Modulus 	1.80 GPa	261 ksi	ISO 527-2/1A
Charpy Impact Unnotched  	NB
@Temperature 23.0 °C	NB
@Temperature 73.4 °F	ISO 179/1eU
 	NB
@Temperature -30.0 °C	NB
@Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched  	3.00 J/cm2
@Temperature -30.0 °C	14.3 ft-lb/in2
@Temperature -22.0 °F	ISO 179/1eA
 	5.00 J/cm2
@Temperature 23.0 °C	23.8 ft-lb/in2
@Temperature 73.4 °F	ISO 179/1eA
 
Electrical Properties	Metric	English	Comments
Volume Resistivity 	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant  	3.2
@Frequency 1.00e+6 Hz	3.2
@Frequency 1.00e+6 Hz	ISO 60250
 	4.1
@Frequency 100 Hz	4.1
@Frequency 100 Hz	ISO 60250
Dielectric Strength 	24.0 kV/mm	610 kV/in	K20/P50; IEC 60423-1
Dissipation Factor  	0.031
@Frequency 1.00e+6 Hz	0.031
@Frequency 1.00e+6 Hz	IEC 60250
 	0.056
@Frequency 100 Hz	0.056
@Frequency 100 Hz	IEC 60250
Comparative Tracking Index 	>= 600 V	>= 600 V	IEC 60093
 
Thermal Properties	Metric	English	Comments
CTE, linear 	270 μm/m-°C
@Temperature 23.0 - 55.0 °C	150 μin/in-°F
@Temperature 73.4 - 131 °F	ISO 11359
Melting Point 	213 °C	415 °F	ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 	170 °C	338 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 	50.0 °C	122 °F	ISO 75
Vicat Softening Point 	175 °C
@Load 5.10 kg	347 °F
@Load 11.2 lb	Method B; ISO 306
Flammability, UL94  	HB
@Thickness 1.60 mm	HB
@Thickness 0.0630 in	IEC 60695
 	HB
@Thickness 3.20 mm	HB
@Thickness 0.126 in	IEC 60695